HOT INFORMATION
<
  • 2018 . 10 . 15
    351
    Daisy
    (1) deformation heat treatment -- the combination of deformation reinforcement and heat treatment enhancement to further improve the strength and toughness of steel.Heat treatment of deformation has high, medium and low temperature.The high temperature deformation heat treatment is to produce the deformation immediately after the austenitic state at a stable distance, or can be combined with forging or hot rolling, that is, quenching immediately after hot forming.The deformation heat treatment has been applied to automobile plate spring production.(60 si2mn)(2) isothermal quenching of spring -- isothermal quenching can be adopted for springs with small diameter or sufficient permeability. It can not only reduce deformation, but also improve strength and toughness. It is better to conduct a...
  • 2018 . 10 . 12
    277
    Daisy
    There are many ways of making spring, but the main forming part is cold forming and hot forming.In spring in the cold forming process, the spring mainly made by oil material toughening, lead bath quenching tempering spring wire, cold drawn wire, etc., using this kind of material in the manufacturing process of spring generally do not need special heat treatment and only requires the stress relieving, adopted by the spring design work stress and material performance.Spring cold forming process is generally suitable for special-shaped spring with small line diameter or more complicated shape, such as line diameter less than 15mm, various kinds of snap, pull, twist spring, convex, concave and arc spring, etc.The cold forming process is simple and avoids the deformation and decarburization of ...
  • 2018 . 10 . 12
    238
    Daisy
    The spring is often corroded by the surrounding medium in the process of manufacture, storage and use.As the spring works under the influence of the spring force, the spring force will change and lose its function after being corroded.Therefore, preventing the corrosion of the spring can guarantee the stability of the spring and extend its service life.The corrosion of spring can be divided into chemical corrosion and electrochemical corrosion according to the type of reaction.They are the result of changes in the metal atoms on the surface of the spring or the loss of electrons to an ionic state.If the metal on the surface of the spring simply reacts with the surrounding medium, causing corrosion of the spring is called chemical corrosion.For example, the spring is oxidized in the particu...
  • 2018 . 10 . 11
    357
    Daisy
    Type of paint used on spring surfacesThe oxidation treatment of the spring (also known as bluish, blackened, cooked black, etc.) is mainly used to prevent the corrosion of the spring, and also to make the spring appearance bright.Oxidation treatment methods include: alkaline oxidation, alkali free oxidation and electrolytic oxidation.Spring oxidation treatment is often alkaline oxidation treatment, in the presence of oxidants (such as sodium nitrite) in caustic sodium solution.As the solution approaches the boiling point, the iron on the surface of the spring dissolves and forms sodium ferrite and sodium ferrite, which is then made of ferrous ironSodium sulfate interacts with sodium ferrite to form magnetic iron oxide (Pe3O4), or oxide film, with a thickness of about 0.5-1.5 microns.The co...
>
INFORMATION
Cooperate with customers to actively develop new products, provide customers with the best r & d team and service quality
Introduction of high precision equipment to improve production technology
News NEWS INFORMATION
HOT INFORMATION / More
64
2018 - 10 - 12
The spring is often corroded by the surrounding medium in the process of manufacture, storage and use.As the spring works under the influence of the spring force, the spring force will change and lose its function after being corroded.Therefore, preventing the corrosion of the spring can guarantee the stability of the spring and extend its service life.The corrosion of spring can be divided into chemical corrosion and electrochemical corrosion according to the type of reaction.They are the result of changes in the metal atoms on the surface of the spring or the loss of electrons to an ionic st...
65
2018 - 10 - 12
There are many ways of making spring, but the main forming part is cold forming and hot forming.In spring in the cold forming process, the spring mainly made by oil material toughening, lead bath quenching tempering spring wire, cold drawn wire, etc., using this kind of material in the manufacturing process of spring generally do not need special heat treatment and only requires the stress relieving, adopted by the spring design work stress and material performance.Spring cold forming process is generally suitable for special-shaped spring with small line diameter or more complicated shape, su...
66
2018 - 10 - 18
With the rapid development of technology, spring's figure is everywhere, playing an irreplaceable role in all walks of life.How to use the properties of the spring itself according to local conditions will be today's small talk about the content.Spring measuring functionWe know that, within the elastic limit, the extension (or contraction) of the stretching spring, compression spring, torsion spring, bending spring, spring and spiral spring is proportional to the force.A spring scale is made from the property of a spring.Spring compression functionObserving various electrical switches, it is f...
67
2018 - 10 - 18
For a long time, the shape and performance of the extension spring will change. If the extension spring is always in a certain situation, it may change its quality due to external conditions.Generally, there are the following situations:I. wear of extension spring :Wear can be divided into abrasive, fatigue and corrosion wear fracture.Ii. Brittle fractureThe majority of spring break belongs to brittle fracture.Plastic fracture is possible only when the working temperature is high.In engineering, fatigue fracture, stress corrosion fracture and hydrogen embrittlement fracture are called brittle ...
68
2018 - 10 - 17
A compact protective film is formed on the surface of the spring by chemical reaction to prevent the corrosion of the spring.Generally, oxidation treatment and phosphating treatment are used.Oxidation treatment and phosphating treatment have low cost and high production efficiency. Generally, spring manufacturers adopt oxidation treatment as corrosion prevention treatment.1.Oxidation treatment of steel is also known as bluing, blackening and boiling black.After oxidation treatment, the surface of the spring produces protective magnetic iron oxide, which is generally blue or black or sometimes ...
69
2018 - 10 - 17
Washing method according to the surface state:General considerationsWhen washing, please pay attention not to scratch the surface to avoid using the bleaching ingredients and the cleaning solution containing abrasive agent, steel ball (brush roller ball), grinding tools, etc. In order to remove the cleaning solution, wash the surface with clean water at the end of washing.Surface condition and washing methodDust and dirt are washed with soap, a mild detergent, or warm waterLabel and film with warm water, weak detergent to scrubThe binder ingredient is alcohol or organic solutionUse a mild clot...
70
2018 - 10 - 16
A, definitions,Spring steel refers to the steel specially used to make spring elastic elements due to its elasticity in the quenching and tempering states.The elasticity of steel depends on its elastic deformation capacity, that is, within the specified range, the elastic deformation capacity makes it bear a certain load, and no permanent deformation occurs after the load is removed.Spring steel shall have excellent comprehensive performance, such as mechanical properties (especially elastic limit, strength limit and yield ratio), anti-elastic and anti-elastic properties (i.e. anti-elastic and...
71
2018 - 10 - 16
The selection of spring material shall be determined according to the properties of the spring bearing load, stress state, stress size, working temperature, environmental medium, service life, requirements for conducting and magnetic conductivity, technical performance, material source and price, etc.When determining the shape and size of the material section, the series sizes specified in the national standards and ministerial standards should be selected first, and non-standard series of materials should be avoided as far as possible.Medium and small-sized springs, especially spiral-tension ...
72
2018 - 10 - 15
There are three ways to use stainless steel spring to remove oil and oxide skin:1. Immerse the stainless steel spring into the plastic container with the metal cleaning agent A diluted with water (the proportion of cleaning agent A and water dilution is 1:1 or 1:2), and the time should be as follows: the spring surface should be free from oil and oxide skin to restore the metal color. The soaking time should not be too long.So stainless steel spring surface has matte effect.2. In the ultrasonic equipment, the proportion of cleaning agent and water is about 1:30. It is advisable to restore the ...
NEW INFORMATION / More
64
2018 - 10 - 17
Washing method according to the surface state:General considerationsWhen washing, please pay attention not to scratch the surface to avoid using the bleaching ingredients and the cleaning solution containing abrasive agent, steel ball (brush roller ball), grinding tools, etc. In order to remove the cleaning solution, wash the surface with clean water at the end of washing.Surface condition and washing methodDust and dirt are washed with soap, a mild detergent, or warm waterLabel and film with warm water, weak detergent to scrubThe binder ingredient is alcohol or organic solutionUse a mild clot...
65
2018 - 10 - 17
A compact protective film is formed on the surface of the spring by chemical reaction to prevent the corrosion of the spring.Generally, oxidation treatment and phosphating treatment are used.Oxidation treatment and phosphating treatment have low cost and high production efficiency. Generally, spring manufacturers adopt oxidation treatment as corrosion prevention treatment.1.Oxidation treatment of steel is also known as bluing, blackening and boiling black.After oxidation treatment, the surface of the spring produces protective magnetic iron oxide, which is generally blue or black or sometimes ...
66
2018 - 10 - 18
For a long time, the shape and performance of the extension spring will change. If the extension spring is always in a certain situation, it may change its quality due to external conditions.Generally, there are the following situations:I. wear of extension spring :Wear can be divided into abrasive, fatigue and corrosion wear fracture.Ii. Brittle fractureThe majority of spring break belongs to brittle fracture.Plastic fracture is possible only when the working temperature is high.In engineering, fatigue fracture, stress corrosion fracture and hydrogen embrittlement fracture are called brittle ...
67
2018 - 10 - 18
With the rapid development of technology, spring's figure is everywhere, playing an irreplaceable role in all walks of life.How to use the properties of the spring itself according to local conditions will be today's small talk about the content.Spring measuring functionWe know that, within the elastic limit, the extension (or contraction) of the stretching spring, compression spring, torsion spring, bending spring, spring and spiral spring is proportional to the force.A spring scale is made from the property of a spring.Spring compression functionObserving various electrical switches, it is f...
68
2018 - 10 - 19
1、 preparation before peening1) the size and surface roughness before spring-shot blasting should meet the requirements of the pattern, except for special instructions (if it is necessary to reprocess the shot blasting surface).2) the spring shall complete the prescribed heat treatment before shot peening.3) the non-destructive test of the spring shall be completed before the shot peening treatment, or after the shot peening if there is special requirement.4) the surface of the spring to be sprayed should be clean, dry and free of oil.2、 treatment after shot peening1) the heating temperature o...
69
2018 - 10 - 19
When the spring is made from materials that do not need to be hardened or tempered after forming, the process is spiral compression spring: rolling, de-stressed annealing, grinding of two ends, (shot blasting), (rectification), (de-stressed annealing), standing or strong pressure treatment, inspection, surface anti-corrosion treatment, packaging.Coil stretching spring: rolling, de-stress annealing, hook making, (cutting the tail), de-stress annealing, standing treatment, inspection, surface anti-corrosion treatment, packaging.Spiral torsion spring: rolling, de-stress annealing, torsion arm mak...
70
2018 - 11 - 03
Internal combustion engine valve spring, low, medium and high stress valve spring, safety valve spring, pressure reducing valve, electric regulating valve, pneumatic regulating valve, self-support regulating valve, hydraulic control valve, steam trap, gate valve, as per valve, butterfly valve, ball valve, check valve, special valve, hydraulic valve, electromagnetic valve, etc.Relief valve: spring safety valve by using the spring force, spring loaded relief valve is closed and not closed in two kinds of structure, general inflammable, explosive or toxic medium should choose enclosed, steam or i...
71
2018 - 08 - 01
Core tips: elastic formula: F=kx, F for elastic, K for the stiffness coefficient, X for the length of the spring length, such as the length of the spring for example, to test a spring of 5N: 5N pull the stiffness coefficient of 100N/m spring, the spring is elongated 5cmF= KX, K is the stiffness coefficient (unit is Newton per meter), X is the spring elongation (unit is rice), this law is called Hooke's law.Elastic formula:F=kx, F is elastic, K is stiffness coefficient, X is spring stretch length.For example, to test a 5N spring:When a spring with a stiffness coefficient of 100N/m is pulled by ...
72
2018 - 08 - 01
The basic spring parameters of the spring:1. Spring wire diameter D: wire diameter of spring.2. The outer diameter of the spring D2: the maximum outer diameter of the spring.3. The inner diameter of the spring D1: the smallest outer diameter of the spring.4. The middle diameter of the spring is D: the average diameter of the spring. Their calculation formula is: D= (D2+D1) +2=D1+d=D2-d5, pitch T: except for the support ring, the distance between the two adjacent circles of the spring corresponds to the axial distance on the middle diameter of the spring, and is expressed by t.6, effective circ...
CONTACT US / More
hotline
86-755-28903525
Room 816, RongChao Financial Center, No 52, RuYi Road,LongCheng Street, LongGang District, ShenZhen,China.
Hot News / 热点新闻
2018 . 11 . 03
点击次数: 259
Internal combustion engine valve spring, low, medium and high stress valve spring, safety valve spring, pressure reducing valve, electric regulating valve, pneumatic regulating valve, self-support reg...
2018 . 11 . 03
点击次数: 248
In the transmission mechanism of the press, when the clutch and the brake adopt mechanical rigid interlock, as long as the air is set on the clutch.The cylinder, the air pressure ACTS on the piston of...
2018 . 11 . 02
点击次数: 360
Zinc electroplating: zinc is stable in dry air and changes little. A white film of zinc oxide or carbon zinc carbonate is formed in moist air. This dense film will prevent further corrosion. Therefore...
作者: Daisy
发布时间: 2018 / 09 / 14
点击次数: 3
55SiCr is the high-grade steel used for automobile suspension springs. The suspension springs bear the reciprocating compression motion in the process of automobile driving, and play the role of buffer and shock absorption, which has high requirements on the performance of steel.Decarburization is one of the main problems in the hot processing of spring steel. Decarburization of spring steel surface will seriously damage the fatigue performance of spring, especially when the total decarburization of ferrite occurs on spring steel surface, the fatigue limit of spring can be reduced by 50%.At present, studies on decarburization of spring steel surface mainly focus on two influencing factors of heating temperature and heating time, while studies on the effect of heating furnace atmosphere on ...
作者: Daisy
发布时间: 2018 / 09 / 14
点击次数: 0
Manufacturers of heat treatment furnaces are adopting new features designed to improve the overall temperature distribution of their equipment: with improved ambient flow patterns, carefully designed energy and dynamic densities have brought very useful working capabilities.Process consistency is a major issue for aerospace (typically, Nadcap and AMS2750 U.S. army standards) and automotive (TS16949 test equipment) customers, and compatibility with more acceptable standards is building confidence between heat treatment equipment manufacturers and customers.This is especially true when the heat treatment furnace design matches the design of the expert process control system.Eurotherm already has a unique knowledge of aviation and automotive heat treatment specifications.These knowledge and s...
作者: Daisy
发布时间: 2018 / 09 / 13
点击次数: 2
The surface of steel is hardenedIn some parts, the surface layer of the workpiece bears higher stress than the core under the action of alternating loads such as torsion and bending and impact loads.In the case of friction, the surface layer is also constantly worn. Therefore, high strength, high hardness, high wear resistance and high fatigue limit are put forward for some surface layer of parts. Only surface strengthening can meet the above requirements.Because surface quenching has the advantages of small deformation and high productivity, it is widely used in production.According to different heating methods, surface quenching mainly includes induction heating, flame heating and electric contact heating.Quench by induction heatingInduction heating is to use electromagnetic induction to...
作者: Daisy
发布时间: 2018 / 09 / 12
点击次数: 5
There are many methods of construction of paint, most of which are used for springs in the following ways:(1) dip coating method dip coating method is to dip the spring into the paint groove, and then take out, and let the excess paint on the surface drip naturally. After drying, it is covered with paint film on the surface of the spring.The dip-coating method has high production efficiency and can be applied to mechanization and automation production.But the paint volatilizes quickly, the paint that contains heavy quality pigment and two component paint material (amine solidify epoxy paint, polyurethane paint etc.) should not be used.Dip coating film is not smooth enough, easy to produce thin and thick, edge flow.(2) spraying method spraying is to use the spray gun to spray the paint into...
作者: Daisy
发布时间: 2018 / 09 / 12
点击次数: 2
Spring machine is now in the production of spring necessary equipment, due to the abundant of spring and the increase of precision is also more and more high to the requirement of spring machine, the spring machine maintenance is particularly important at ordinary times, and the main factors affecting the service life of spring machine has two, one is the operator of whether scientific and standardized operation, another is reasonable in daily maintenance.After using the spring machine for a period of time, the efficiency of the machine will be significantly reduced, affecting the efficiency of production. At this time, we should pay attention to the maintenance of the machine parts. Some seriously worn parts should be replaced in time.In the process of use, the inner part of the spring ma...
作者: Daisy
发布时间: 2018 / 09 / 11
点击次数: 4
Vibration damping spring is a common elastic component, which is widely used in various vibration equipment and automobile manufacturing industries. It has the advantages of good stability, low noise, good isolation effect and long service life.Compression springs, rubber springs, composite springs, air bag springs are vibration - reducing springs.Vibration damping spring can be divided into: wire compression spring, rubber spring, compound spring, rubber air spring, etc.Steel wire compression spring is a spiral spring under pressure, it USES the material section is mostly circular, also USES the rectangle and the multi-strand steel entangle to coil.Spring is commonly pitch, such as the shape of the compression spring are: cylindrical, conical, convex and concave and a small amount of rubb...
作者: nelson
发布时间: 2018 / 09 / 11
点击次数: 1
Like most other basic mechanisms, metal springs have existed for a long time in the bronze age. Even for metals, wood is used as a structural member of flexible bow and arrow and military catapult. In the Renaissance, precise clocks made precision springs the first necessity. In Fourteenth Century, we saw the precise clock of revolutionary astronomical navigation developed. The world's exploration and conquest of European colonial powers continue to provide impetus for watchmakers "science and art." The other area of the firearm promotes the development of the spring. At the dawn of the industrial revolution in eighteenth Century, a large, accurate and cheap spring was proposed. Whereas the watchmaker's spring is often made by hand, the spring mass production is made of piano ste...
作者: Daisy
发布时间: 2018 / 09 / 10
点击次数: 5
The corrosion of spring can be divided into chemical corrosion and electrochemical corrosion according to the type of reaction.They are the result of changes in the metal atoms on the surface of the spring or the loss of electrons to an ionic state.If the metal on the surface of the spring simply reacts with the surrounding medium, and the spring causes corrosion, it is called chemical corrosion.For example, the spring is oxidized in the particularly dry atmosphere to form an oxidation film, and the spring is chemically changed with the liquid or impurity in the non-electrolyte liquid, which is a chemical corrosion.If the spring is in contact with the electrolyte solution, the corrosion caused by the action of the micro battery is called electrochemical corrosion.For example, the spring is...
作者: nelson
发布时间: 2018 / 09 / 10
点击次数: 2
Spring grinding is easy to produce cracks at the end of the tightness, and directly affect the verticality of the spring, load and free length size, so the general grinding process of spring should be carried out after stress relief tempering. Eliminate the residual stress of steel wire cold drawing to prevent the generation of end gap cracks.The main factors that affect the quality of springs in grinding are as follows:(1) The grinding wheel should be selected reasonably; (2) the control of the bevel angle of the end ring; (3) a certain number of special measuring tools should be equipped to ensure the grinding quality; (4) the grinding wheel should be repaired in time; (5) the correct size of the grinding sleeve should be selected, and the gap between the spring and the sleeve should be ...
143页次8/16首页PrePage...  3456789101112...NextPage尾页
Copyright ©2018 AFR PRECISION TECHNOLOGY CO,LTD
Xiniuyun Providing enterprise cloud services
在线聊天
live chat
-->
客户服务
live chat