Please avoid the improper way of using (1) more than the use of the maximum compression (300000 back to the conditions, after a close with the use of a long) stress causing the wreck, close to close with the use of a long, can make the spring line department gradually close to that, because of the high spring constant change caused by load curve with high, nearly and produce high stress to make spring break, please do not use more than 300000 times.The use of the spring without prepressure due to the gap caused the spring up and down vibration caused the spring distortion, if there is prepressure, the spring is relatively stable.When the spring is used, the pin and the spring will be worn and broken.When used without spring guide, the bottom of the spring and the body of the spring are easily distorted. The high pressure of the twisted part is the main cause of spring breaking.
When the assembly surface is poor in flatness, the poor parallelism of the assembly surface will result in spring distortion, local high pressure fracture, and in the case of poor parallelism, it will result in spring distortion and over 300,000 times of use, resulting in spring fracture.Please improve the parallelism of the mounting surface under the condition of no more than 300,000 reuses.If the gap between the inner diameter of the spring and the guide pin and the guide pin is too small, it will cause the collision and wear of the inner diameter. The wear part is the main reason for the spring break.And spring with long free length (free length/outside diameter greater than 4) please use step or pin to avoid collision with the pin when the spring body is twisted.When the outer diameter of the main spring and the countersunk hole and the spring-gap head are too small, the lateral expansion due to the compression of the spring and the friction of countersink hole will result in concentrated force fracture. The better countersink hole diameter is +1.5mm.Use the countersink hole shape for long free springs.The length of the pin and the depth of the sunk hole are too short, which will cause the pin head to break with the spring. The ideal length of the pin is set to more than 1/2 of the length of the spring.When the spring is deflected or used, the force exerted on the spring causes the inner coil spring to be inserted into the outer ring (or the outer ring to be inserted into the inner ring) to break.When the spring is used in series connection, the spring bends and exceeds the length of the pin or the hole of the sinking head, resulting in a fracture of the same reason, and a slightly different load of the spring, resulting in a larger compression surface fracture than the weak one.When foreign body inclusion is used, foreign body inclusion part will cause the effective roll part to have no effect but the compression of other parts. The actual effective winding number decreases, and the near side will cause high stress and fracture. Do not include foreign body in the spring.